Electrochemical Impedance of Hydrogenated Phases of ZnO and CuO Nanoparticles for Electrode Applications
L. I. Menegbo
Department of Chemistry, Rivers State University, Nkpolu-Oroworukwo, Port Harcourt, Nigeria.
J. L. Konne *
Department of Chemistry, Rivers State University, Nkpolu-Oroworukwo, Port Harcourt, Nigeria.
N. Boisa
Department of Chemistry, Rivers State University, Nkpolu-Oroworukwo, Port Harcourt, Nigeria.
*Author to whom correspondence should be addressed.
Abstract
The Electrochemical Impedance Spectroscopy (EIS) measurements of Sol-gel synthesized ZnO, CuO and their respective hydrogenated phases (ZnO:H and CuO:H) for a proton-type battery model has been reported for the first time. The XRD patterns confirmed that CuO and ZnO were phase pure with minor impurities. However, that of CuO:H showed mixed phases of CuO and Cu2O with the later appearing prominent. The estimated particle sizes of ZnO, ZnO:H, CuO and CuO:H obtained using Scherrers’ equation were 17.83, 17.75, 21.63 and 15.42 nm respectively, showing remarkable particle size reductions upon hydrogenation as oxygen vacancies were substituted with smaller hydrogen ions. Nyquist plots from the EIS experimental data recorded over a frequency range of 100 kHz – 5 mHz showed expected flat semicircles at the high frequency region and straight lines at the low frequency regions while resistance estimations from the intercepts of the Bode plots were 12.10, 7.80, 16.00 and 10.80 Ω for ZnO, ZnO:H, CuO and CuO:H respectively. It also indicated high gain margins suggesting impressive electrochemical properties for battery applications.
Keywords: Defects, sol-gel preparation, battery, ZnO/ZnO:H, CuO/CuO:H, EIS (Nyquist &Bode).